Elemental analyses of the samples are summa-rized in Table 1.The most striking feature of the results is that the content of aluminum ions decreased progressively while that of silicon ions increased as crystallization proceeded.The increase in silicon content can be explained by a loss of colloidal silica particles at the washing stage of the samples; however,the decrease in aluminum samples; however,the decrease in aluminum content is rather puzzling and may be explained by the presence of excess aluminum ions as boehm-ite gel particles while some part of the phosphate ions are present in solution.
From the results mentioned above we suggest the following scheme for the crystallization of Ni-SAPO-34 by the rapid crystallization method.
(1) At the early stage of the crystallization,an aluminophosphate-like framework is formed.Most of the silicon ions are present as colloidal silica particles.At this stage,Ni2+ ions are present as octahedral coordination and presumably are occluded in the defects of SAPO-34.
(2) Crystallization proceeds with increasing temperature and silicon ions begin to be incorporated into the framework.Ni2+ ions fall into the tetrahedral sites,forming Ni-SAPO-34 at the final stage of the crystallization.
Elemental analyses of the samples are summa-rized in Table 1.The most striking feature of the results is that the content of aluminum ions decreased progressively while that of silicon ions increased as crystallization proceeded.The increase in silicon content can be explained by a loss of colloidal silica particles at the washing stage of the samples; however,the decrease in aluminum samples; however,the decrease in aluminum content is rather puzzling and may be explained by the presence of excess aluminum ions as boehm-ite gel particles while some part of the phosphate ions are present in solution.
From the results mentioned above we suggest the following scheme for the crystallization of Ni-SAPO-34 by the rapid crystallization method.
(1) At the early stage of the crystallization,an aluminophosphate-like framework is formed.Most of the silicon ions are present as colloidal silica particles.At this stage,Ni2+ ions are present as octahedral coordination and presumably are occluded in the defects of SAPO-34.
(2) Crystallization proceeds with increasing temperature and silicon ions begin to be incorporated into the framework.Ni2+ ions fall into the tetrahedral sites,forming Ni-SAPO-34 at the final stage of the crystallization.
我的翻译是:甲醇制烯烃合成过程中的镍SAPO-34催化剂 Masashi Inoue *,用镍SAPO-34催化剂进行甲醇-烯烃转化的合成过程摘要通过快速结晶法制备的镍,
英语翻译Elemental analyses of the samples are summa-rized in Tab
英语翻译In-oui analyses of the fragrances data,we replicated the
英语翻译The bivariate analyses in figure 5 support the associati
英语翻译Elemental needs have been sacrificed in the West by the
英语翻译Speciation-saturation analyses of the reacted solutions
英语翻译Analyses of the certified reference material CRM 463 sho
英语翻译In this study,the preliminary correlation analyses have
英语翻译Statistical analyses were performed in the intent-to-tre
英语翻译3) The most common samples of inorganic materials are th
The most common samples of inorganic materials are the gases
英语翻译What are the differences between Chinese and western tab
英语翻译The measurement results of the samples and first deliver